This paper presents the results of research which is part of studies carried out under the project POIG.01.01.02-00-015/09 "Advanced Materials and Technologies", one of the aims of which is to introduce new, environment-friendly, inorganic binders to the production of castings from non-ferrous metals. The paper presents the results of research on the management of waste moulding sands prepared according to the new technology, including their multiple reclamation and management of post-reclamation waste. Studies of multiple reclamation are a continuation of the preliminary research described earlier. The programme of the studies described in this paper also included validation of the results under industrial conditions.
The results of mechanical reclamation of waste moulding sands with furfuryl resin and activators of new generation are presented. The aim of the research described in this study was to determine what effect the addition of reclaim obtained in the process of dry mechanical reclamation could have on the properties of furan sands. The sand supplied by one of the domestic foundries was after the initial reclamation subjected to a two-step proper reclamation process. The following tests were carried out on the obtained reclaim: pH, S and N content, loss on ignition and comprehensive sieve analysis. The obtained reclaim was next used as a component of moulding sands with furfuryl resin, wherein it formed 50% and 80% of the base moulding material, respectively. The strength properties of the ready sand mixtures (bending strength Rg u and tensile strength Rm u ) were determined after the hardening time of 0.5, 1, 2, 4 and 24 hours.
One of the factors that contribute to the development of foundry moulding technology is environmental protection. The related challenges are effectively satisfied by a new inorganic binder that has been designed for castings made of non-ferrous metal alloys. This article presents in a concise way the test results, showing the ecological character of the new binder at the stage of making moulds, pouring them with metal and cooling of castings, indicating the possibilities for an economic re-use of waste materials formed during practical application of this technology. The results were compared with the results obtained on the sands with organic binders. Studies were carried out under the project POIG.01.01.02-00-015/09 "Advanced materials and technologies."
In the family of iron-based alloys, ductile iron enjoys the highest rate of development, finding application in various industries. Ductile iron or the cast iron with spheroidal graphite can be manufactured by various methods. One of them is the Inmold spheroidization process characterized by different technological solutions, developed mainly to increase the process efficiency. So far, however, none of the solutions has been based on the use of a reactor made outside the casting mould cavity. The method of spheroidization inside the casting mould using a reaction chamber developed at the Foundry Research Institute is an innovative way of cast iron treatment. The innovative character of this method consists in the use of properly designed and manufactured reactor placed in the casting mould cavity. Owing to this solution, the Inmold process can be carried out in moulds with both horizontal and vertical parting plane. The study presents the results of examinations of the microstructure of graphite precipitates and metal matrix of castings after spheroidization carried out by the Inmold process using a reactor and mould with vertical parting plane. Special pattern assembly was made for the tests to reproduce plates with wall thicknesses of 3; 5; 7; 10; 20 and 30 mm. The content of residual magnesium was determined for all tested castings, while for castings of plates with a wall thickness equal to or larger than 10 mm, testing of mechanical properties was additionally performed.
The effectiveness of cast iron spheroidization with FeSiMg master alloy by the traditional method and using a reaction chamber placed in the cavity of foundry mould was compared. The method of cast iron treatment in mould cavity using a reaction chamber is an innovative technology developed by the Foundry Research Institute in Krakow. The effectiveness of the spheroidization process carried out by both methods was checked on a series of test castings. The article also presents the results of metallographic examinations and mechanical testing, including the discussion of magnesium yield and its assimilation rate.
The aim of the study was to determine the applicability of a new product added to water glass-containing foundry sands hardened with ethylene glycol diacetate. The new additive designated by the symbol "B" is a composition of aqueous solutions of modified polyalcohols, improving the sand knocking out properties. The scope of studies included testing various mechanical and technological properties of foundry sand mixtures, such as permeability, friability, life cycle of cores and knocking out properties. In the technological studies, two types of water glass with different values of the silica modulus and density, designated as R145 and R150, were used. Moulding sands were prepared with the additive "B". For comparison, reference sands with water glass but without the additive "B" were also made. In Part I of the article, the results of studies of the effect of additive "B" on the properties of foundry sands with water glass hardened by CO2 blowing were discussed.